ガス腐食試験
国際的なガス腐食試験規格の例
| 規格 | 試験の種類 | ガスの種類と濃度（ppm） | 温度および湿度 | |||
|---|---|---|---|---|---|---|
| H2S | Cl2 | NO2 | SO2 | |||
| ISO10062 Corrosion tests in artificial atmosphere at very low concentration of polluting gas | Method A | ― | ― | ― | 0.5±0.1 | 25±1℃ 75±3％RH |
| Method B | 0.1±0.1 | ― | ― | ― | ||
| Method C | 0.1±0.1 | ― | ― | 0.5±0.1 | ||
| Method D | 0.1±0.1 | 0.02±0.005 | ― | 0.5±0.1 | ||
| IEC60068-2-42 Basic environmental testing procedure Part2：Test Kc：Sulfur dioxide test for contacts and connections（1982） | ― | ― | ― | 25±5 | 25±1℃ 75±3％RH |
|
| IEC60068-2-43 Basic environmental testing procedure Part2：Test Kd：Hydrogensulohide test for contacts and connections | 10～15 | ― | ― | ― | 25±1℃ 75±3％RH |
|
| IEC60068-2-60 Environmental testing－Part2：Tests－ Test Ke：Flowing mixed gas corrosiontest | Method 1 | 0.1±0.02 | ― | ― | 0.5±0.1 | 25±1℃ 75±3％RH |
| Method 2 | 0.01±0.005 | 0.01±0.005 | 0.2±0.005 | ― | 30±1℃ 70±3％RH |
|
| Method 3 | 0.1±0.02 | 0.02±0.005 | 0.2±0.05 | ― | 30±1℃ 75±3％RH |
|
| Method 4 | 0.01±0.005 | 0.01±0.005 | 0.2±0.02 | 0.2±0.02 | 25±1℃ 75±3％RH |
|